| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 熔體流動速率 | 125℃/2.16kg | ASTM D-1238 | 65 | g/10min |
| 熔體流動速率 | 125℃/2.16kg | ISO 1133 | 65 | g/10min | |
| 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 1300 | g/10min | |
| 熔體流動速率 | 190℃/2.16kg | ISO 1133 | 1300 | g/10min | |
| 單體含量 | Internal Method | 20 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.955 | g/cm3 | |
| 比重 | ISO 1183 | 0.955 | g/cm3 | ||
| 機械性能 | 拉伸模量-2% Secant | Compression Molded | ASTM D-638 | 22.1 | MPa |
| 拉伸模量-2% Secant | Compression Molded | ISO 527-2 | 22.1 | MPa | |
| 拉伸斷裂強度 | Compression Molded | ASTM D-638 | 6.21 | MPa | |
| 拉伸斷裂強度 | Compression Molded | ISO 527-2 | 6.21 | MPa | |
| 拉伸斷裂伸長率 | Compression Molded | ASTM D-638 | 350 | % | |
| 拉伸斷裂伸長率 | Compression Molded | ISO 527-2 | 350 | % | |
| 熱性能 | 維卡軟化點 | ASTM D-1525 | 40 | ℃ | |
| 維卡軟化點 | ISO 306 | 40 | ℃ | ||
| 熔融溫度 | Internal Method | 75 | ℃ | ||